[robert hackert]

This is why I use either an oatmeal liner or a temmoku liner. Doing this long before this latest notification.
Kind regards,

Robert Hackert

Sent from my iPhone

> On Nov 8, 2016, at 1:45 PM, "ronroy at ca.inter.net" <ronroy at ca.inter.net> wrote:
> 
> Hi Doug,
> 
> This is not aimed at you - I was just waiting to tell this story about the subject.
> 
> This is an unusual example but I'll bet you could find examples close to this without too much trouble.
> 
> I was buying some supplies at a local supplier and the owner asked me into his office to show me a mug. It was glazed with a barium matte coloured with cobalt - an intense blue - inside and out.
> 
> About half way up from the bottom inside the glaze was white - pure white - no blue!
> The owner of the mug had left it overnight half filled with neo-citron - a cold relief remedy. A powder mixed with water sold in Canada - maybe in the US as well?
> 
> All the cobalt had been leached out of the glaze along with some of the Barium and whatever else was in the glaze.
> 
> Imagine how the owner felt about the potter who made that mug - especially if they also had the current information about cobalt being a carcinogen? Imagine how that person now felt about hand made pottery.
> 
> At best it's an excellent argument to limit colour in liner glazes especially if  there is little interest in glaze durability on the part of the maker.
> 
> RR
> 
> 
> Quoting Douglas Fur <23drb50 at gmail.com>:
> 
>> I looked at the report. What they are concerned about seems to be water
>> soluble cobalt compounds which might release cobalt metal ions inside the
>> body. I didn't see any density level or threshold level.
>> 
>> Practically speaking we use cobalt oxide in very small amounts not cobalt
>> metal. Cobalt oxide is rated as insoluble or slightly soluble in water. If
>> you've used cobalt to mark glaze tests you may have noticed a sheen on the
>> surface after it is fired. This is where the CoO has reacted with the SiO2
>> to form cobalt silicate. I couldn't find a reference to the water
>> solubility of cobalt silicate but my sense is that if cobalt is so reactive
>> with silica  that it fuses with the silica in a clay body it's not likely
>> very soluble in water.
>> 
>> Since we don't use  cobalt compounds noted for solubility in water and we
>> use relatively small amounts of cobalt compounds which, once fired they
>> seem to be firmly bound in the glaze, I don't think we need to be concerned
>> about cobalt release from our pots.
>> 
>> Maybe in a situation where cobalt decoration is painted on the glaze
>> surface you might have a local condition where the glaze is overloaded but
>> even then it seems like you would more likely have insoluble cobalt oxide
>> than a soluble cobalt compound.
>> 
>> This has more speculation than facts so my summary would be don't panic but
>> get more facts.
>> 
>> Duff
>> Seola Creek
>> -------------- next part --------------
>> An HTML attachment was scrubbed...
>> URL: <http://lists.clayartworld.com/pipermail/clayart/attachments/20161107/3597511a/attachment.html>
>> 
>> 
> 
> 
> 
> Ron Roy
> ronroy at ca.inter.net
> Web page ronroy.net
> 
> 
>